PURE TANTALUM FOIL R05200 Shenzhen Sunrise Metal Industry Co.,Ltd
0086-0755-27185042
http://www.sunriseta.com
sales@sunriseta.com
http://www.sunriseta.com
sales@sunriseta.com
skype :Li.mary9
QQ :1957953030
wahtsapp: 15919982500Material:tantalum foil according to ASTM B708 RO5200
Size:0.05*200*coil
Quantity:1.5kg
CIF Price:760 USD/KG
Size:0.1*120*coil
Quantity:1kg
CIF Price:730 USD/KG
Size:1.5*300*300mm
Net weight:2.25kg/pc
CIF Price:1,428 USD/PC
Size:2*300*300mm
Net weight:3kg/pc
CIF Price:1,905 USD/PC
The lead time:20days after confirm this order.
Tantalum sheet
we can produce 1-meters width and 5-meters long annealed tantalum sheet,our tantalum price is competitive.
Product details
Tantalum sheet, Tantalum plate, Ta10w tantalum plate, Spinneret tantalum sheet
Purity : 99.95％min or 99.99％min conformity with ASTM B 708 98
Size:
Thickness (mm) Width (mm) Length (mm)
Foil 0.03-0.07 30-200 >50
Sheet 0.07-0.5 30- 700 30-2000
Board 0.5-10 50-1000 50-3000
Purity: >=99.95％ or 99.99％
Size:
Thickness (mm) Width (mm) Length (mm)
Foil 0.03-0.07 30-200 >50
Sheet 0.07-0.5 30- 700 30-2000
Board 0.5-10 50-1000 50-3000
Purity: >=99.95％ or 99.99％
Table 1:Chemical composition
Table 2. Mechanical requirements (annealed condition)
Table 2. Mechanical requirements (annealed condition)
Grade and size
|
Annealed
| ||
Tensile strength
min， psi (MPa)
|
Yield strength min，psi (MPa)(2％)
|
Elongation min， ％ (1 inch gage length)
| |
Sheet， foil. and board (RO5200， RO5400) Thickness<0.060"(1.524mm)
Thickness≥0.060"(1.524mm)
|
30000 (207)
|
20000 (138)
|
20
|
25000 (172)
|
15000 (103)
|
30
| |
Ta-10W (RO5255)
Sheet， foil. and board
|
70000 (482)
|
60000 (414)
|
15
|
70000 (482)
|
55000 (379)
|
20
| |
Ta-2.5W(RO5252)
Thickness<0.125" (3.175mm)
Thickness≥0.125" (3.175mm)
|
40000 (276)
|
30000 (207)
|
20
|
40000 (276)
|
22000 (152)
|
25
| |
Ta-40Nb (RO5240)
Thickness<0.060"(1.524mm)
|
40000 (276)
|
20000 (138)
|
25
|
Thickness>0.060"(1.524mm)
|
35000 (241)
|
15000 (103)
|
25
|
Applications
Using Tantalum sheet or Tantalum plate in Machinery and Chemical Processing.